PENGARUH TEMPERATUR ANNEALING TERHADAP SIFAT FISIS BATU BATA LIMBAH  SERAT  ALAMI

ARTHA NESA CHANDRA; Djusmaini Djamas; Ramli Ramli

doi:10.31958/js.v8i2.476

PENGARUH TEMPERATUR ANNEALING TERHADAP SIFAT FISIS BATU BATA LIMBAH SERAT ALAMI

ARTHA NESA CHANDRA, Djusmaini Djamas, Ramli Ramli

Abstract

This study aims to determine at what temperature annealing which will produce compressive strength and good porosity in the brick waste natural fiber. This study was an experimental study with dick variables such as the proportion of clay and waste of natural powder that is 90%: 10%, each grain size 0.18 mm material, waste natural powder used is sawdust sawmill. The independent variable is the temperature annealing while the dependent variable is the compressive strength and porosity. And wastes natural clay powder mixed and given 5 liters of water, then in print square shaped measuring 6x6x6 cm by 20 pieces to determine the compressive strength and the cylinder-shaped measuring 10 x 7 cm by 4 units to determine the value of porosity. Each of these samples with variations in-Anneal Annealing temperature 7000C, 7500C, 8000C and 8500C using Electric Furnace. After data collection and data analysis of compressive strength and porosity of the importance of the value of the maximum compressive strength of 89.5 kg / cm2 at a temperature of 8500C and this value meets the standards. While the minimum porosity value was 2.10% at the temperature of 8500C.

Keywords

bricks waste of natural fibers, annealing temperature, porosity, compressive strength

Full Text:

Download PDF (Bahasa Indonesia)

References

Amir AH. 2002. Pemanfaatan Limbah untuk Bahan Bangunan. Bandung: Modul Puslitbang Pemukiman.

Anshar M, Anwar M dan M Idris. 2001. Perilaku Suhu dan Waktu Pembakaran Terhadap Ciri Batu Bata Merah, http://www.dikti.org/p3m/3.html.

Basri LH. 1986. Pemanfaatan Sekam Untuk Bahan Bangunan, Kertas Kerja Perorangan, Deperin Sumbar.

Bowles. Joseph E. 1991. Sifat- Sifat Fisis Dan Geoteknis Tanah (Mekanika Tanah). Jakarta: Erlangga.

Dewan Standardisasi Nasional. 1991. SNI 15-2094-1991. Mutu dan Cara Uji Bata Merah Pejal, Jakarta.

Dieter GE. 1996. Metalurgi Mekanik, edisi ketiga, terjemahan Sriati Djaprie. Jakarta: Erlangga.

Handayani S. 2010. Kualitas Batu Bata Merah dengan Tambahan Serbuk Gergaji. Jurnal Teknik Sipil dan Perencanaan. Nomor 1 Volume 12-Januari 2010, Hal:41-50.

Hartomo. Anton J. 1994. Mengenal Keramik Canggih. Yokyakarta: Andi Offset.

Harsono, Heru. 2002. Pembuatan Silikon Amorf dari Limbah Sekam Padi, Jurnal ILMU DASAR, Vol.3,No.2,2002 hal 98-103.

Indra, Ade. 2013. Pengaruh temperatur Pembakaran Pada Komposit Lempung/Silika RHA terhadap Sifat Fisis (Aplikasi pada Bata Merah), Jurnal Teknik Mesin Volume 3 Nomor 2 Oktober 2013, Hal:60-65.

Kemino. 1995. Penelitian Pemanfaatan Limbah Industri Pengolahan Kayu Sebagai Bahan Baku Pembuatan Bata Cetak. Jurnal Penelitian Permukiman, Vol.11-7/1995.

Manggasa A, dkk. 1996. Pengembangan Teknologi Pengolahan Serbuk Gergaji Sebagai Bahan Pengisi Pada Pembuatan Bata Cetak, Laporan Proyek, Balai Industri Ujung Pandang.

Munandar M. 2001. Ketentuan Dinding Tembok Wilayah Gempa, Buletin Pengawasan No.30&31 Th 2001.

Nada I made. 2013. Karakteristik Fisik Campuran Batu Bata dengan Memanfaatkan Abu Sisa Pembakaran Limbah Kayu, Kurva Teknik Vol 2, No 1 (2013): Jurnal Kurva Teknik Volume 2 Nomor 1 Tahun 2013, Hal: 88-97.

Rahmawati, Anis, dkk. 2015. Penambahan Abu Jerami dan Abu Sekam pada Campuran Batu Bata untuk Meningkatkan Kualitas dan Efisiensi Produksi Batu Bata Industri Tradisional, Jurnal Eco Rekayasa Volume 11 Nomor 1, Maret 2015, Hal:16-22.

SII/DP/BPPI/BBK/73/78 Mutu Dan Cara Uji Lempung. Bandung.

SII No 0021-78 Mutu Dan Cara Uji Batu Bata Merah Pejal. Padang.

Suryaningsih. 2005. Karakterisasi Fisis Lempung yang Terdapat di Daerah Payakumbuh dan Padang Sibusuk Untuk Body Keramik, Skripsi. Universitas Negeri Padang.

Sutopo.1987. Ilmu Bangunan. Jakarta: Bumi Aksara.

Van.Valack Lawrence. 1992. Ilmu dan Teknologi Bahan. Jakarta: Erlangga.

DOI: http://dx.doi.org/10.31958/js.v8i2.476